Home > Products > High polymer membrane > High polymer polyethylene waterproofing membrane > The PP-PE waterproof membrane .....
Browse Categories
Home improvement eco-friendly materials(12)
Self-adhesive waterproofing tape(109)
Modified bitumen membrane(116)
High polymer membrane(302)
Geotextile & Geomembrane(50)
Waterproof Raw Material(43)
Waterproof Production Lines(10)
Pu Painting,Coating,Primer and Emulsion(28)
Asphalt Saturated Felt(10)
Self-adhesive bitumen membrane(96)
Certifications
Contact us
China Address: Zhengyang Road, Shouguang City, Shandong Province, ChinaTel:+86 18366529777Fax:+86 05365511977 E-mail:admin@dongshengwaterproof.com
Contact Now
The PP-PE waterproof membrane manufacturerThe PP-PE waterproof membrane manufacturerThe PP-PE waterproof membrane manufacturer

The PP-PE waterproof membrane manufacturer

  • Min .order Quantity:2000 Square Meters
  • Supply Ability     :3 000000 Square Meters/ per Month
  • Port               : QINGDAO PORT
  • Payment Term      :L/C,T/T
  • thickness          :400g-1500g/ Square Meters
  • width              :1.0-1.2mm
  • length              :100m

Product Overview 

It is high polymer waterproof sheet with high polymer fibre as reinforcement adhesive layer, and extrusion.

 

Features

1.The polymer fiber-reinforced adhesive layer makes full adhesion between polymer cement waterproof adhesive material and the base course.

2.Polymer cement waterproof adhesive material can be used to fill holes and rough or uneven parts, which prevents water channeling of adhesive layer and plays an auxiliary role in waterproofing.

3.The full adhesion between polymer cement waterproof adhesive material and base course help 4.The sheet can be designed designed directly  in cement structure and used on surfaces of adhesive titles and plastering.

5.The product has great anti-puncture performance and therefore is employed in waterproof gardening roof and resistant to puncture by plant roots.



Performance index

Performance conforms to polymer water-proof materials-section one :Sheet(GB 18173.1-2012)

 

No

item

index

Vulcanized rubber FL

Non-Vulcanized

Resinous

FS1

FS2

1

 

Tensile strength at break/(N/cm)

Normal temperature(23℃)≥

80

60

100

60

High temperature(60℃)≥

30

20

40

30

2

Elongation at break /%

Normal temperature(23℃)≥

300

250

150

400

Low temperature(-23℃)≥

150

50

-

300

3

Peel strength/N   ≥

40

20

20

50

4

Watertight (0.3MPa ,30min)

No leakage

No leakage

No leakage

No leakage

5

Fold ability at low temperature

-35℃

No crack

-35℃

No crack

-35℃

No crack

-35℃

No crack

6

Heat elongation and shrinkage/mm

Elongation ≤

2

2

2

2

Shrinkage ≤

4

4

4

4

7

Air aging(80℃*168h)

Retention of tensile strength at break%≥

80

80

80

80

Elongation retention at break%≥

70

70

70

70

8

Alkali-resistance 

Retention of tensile strength at break%≥

80

60

80

80

Elongation retention at break%≥

80

60

80

80

9

Ozone aging, elongation 20%

No crack

No crack

--

--

10

Artificial weathering

Retention of tensile strength at break%≥

80

70

80

80

Elongation retention at break%≥

70

70

70

70

11

Adhesive peeling strength(sheet with sheet)

Standard test conditions(N/m)≥

1.5

1.5

1.5

1.5

Retention after water immersion(23℃*168h)/%≥

70

70

70

70

12

Composite strength( FS2 surface and central layer)/MP a≥

__

__

__

0.8

 

 

Scope of Application 

1.Used for waterproofing, damp proofing and gas insulation in roofing, basement, washing room and walls.

2.Used for waterproofing and anti-seepage in construction of roads ,railway, subway, bridges and culverts ,caves, tunnels.

3.Used for waterproofing and anti-seepage in refuse landfill, sewage farms, anti-pollution in chemistry metallurgy ,pipes and mines.

 

Construction  methods

Choosing adhesion

Choose matched polymer dry power adhesive material and polymer cement waterproof adhesive material made of ordinary port land cement for bonding of sheets.

Way of jointing 

Lap joint is employed. Lap joint with Cover filler applies to comparatively important engineering. Butt joint with filler strip is used for single-face composite products. Thick products can be welded.

Base treatment ,the base course shall be treated and cleared. make sure to dust, water and oil stains can be seen on the base course .Protuberance and mortar lumps shall be cleared away. 

Pavement

1.place 3m to 8m in advance at the position where sheet will be paved. after alignment, fix it at the central part after alignment .Roll one end of the sheet to the fixed part and coat it with glue. After adhesion is finished for one end . Roll the other end to the fixed part and glue it .Pave it continuously until all the sheet is finished.

2.During pavement ,use a scraper to scraper the adhesive material to the surface of base course and sheet and then paste the sheet .Meanwhile ,use a scraper or compression roller to elminate the air and press the sheet hard to squeeze  out the unnecessary adhesive material.

3.As to construction on vertical surfaces, alignment must be guaranteed to avoid inclined pavement and press from bottom to the top to squeeze out the air.


 