Home > Products > High polymer membrane > TPO > TPO roof waterproof material s.....
Browse Categories
Home improvement eco-friendly materials(12)
Self-adhesive waterproofing tape(109)
Modified bitumen membrane(116)
High polymer membrane(302)
Geotextile & Geomembrane(50)
Waterproof Raw Material(43)
Waterproof Production Lines(10)
Pu Painting,Coating,Primer and Emulsion(28)
Asphalt Saturated Felt(10)
Self-adhesive bitumen membrane(96)
Certifications
Contact us
China Address: Zhengyang Road, Shouguang City, Shandong Province, ChinaTel:+86 18366529777Fax:+86 05365511977 E-mail:admin@dongshengwaterproof.com
Contact Now
TPO roof waterproof material supplierTPO roof waterproof material supplierTPO roof waterproof material supplier

TPO roof waterproof material supplier

  • Min.order Quantity :3000 Square Meters
  • Supply Ability     :3000000 Square Meters/ per Month
  • Port               :QINGDAO PORT
  • Payment Term       :L/C,T/T
  • thickness          :1.5mm
  • width              :1.0m,1.2m,2.0m,2.05m
  • length             :20m
  • (Above quantities are indicative only. We can produce it according to your demands).

(DS-H-TPO) Thermoplastic Polyolefin
Waterproofing Membrane

Product description > > > 

Thermoplastic polyolefin (TPO) waterproof membrane is based on the use of advanced polymer technology will be ethylene propylene rubber and polypropylene together with the thermoplastic polyolefin (TPO) synthetic resin as the base material, adding antioxidant, antioxidant, softener system Into a new type of waterproof membrane, can be made of polyester fiber mesh cloth made of enhanced internal waterproofing membrane waterproof material, synthetic waterproofing membrane waterproofing products are waterproof.

 

Feature > > >

PO waterproof membrane integrated TEPDM and PVC performance advantages, with the former weathering ability, low temperature flexibility and the latter can be welded characteristics. This material is different from the traditional plastic, at room temperature shows high elasticity of rubber, at high temperatures and can be molded like plastic. Therefore, this material has good processing performance and mechanical properties, and has high-strength welding performance. In the middle of two layers of TPO material with a layer of polyester fiber, can enhance its physical properties, improve its fracture strength, anti-fatigue, anti-puncture ability.

In practice, the thermoplastic polyolefin (TPO) waterproof membrane width wide, faster construction, lap joints with hot air welding method, the overall tightness. Construction is not affected by hot and cold climate, easy maintenance, recyclable materials, meet environmental requirements and competitive prices and other factors. TPO waterproofing membrane application in China is also more and more widely, is the single-layer waterproof roofing one of the fastest growing materials. The product name with anti-aging, tensile strength, elongation, wet roof can be constructed. No leakage protection layer, convenient construction, no pollution and other comprehensive features, is very suitable for use as a light-weight waterproof roof waterproofing.

 

Classification > > >

According to the composition of the product is divided into homogeneous composite coil (H), backing with fiber composite coil (L) and enhancing the organization within the coil (P), glass fiber enhanced coil (G), glass fiber reinforced with fiber backing composite coil (GL) of the

 

specification> > >

 

Nominal length specifications for: 15 m, 20 m, 25 m

Nominal width specifications for: 1.00 mm, 2.00 mm

Specifications for thickness: 1.20 mm, 1.50 mm, 1.80 mm and 2.00 mm

 

Scope application > > >

Applied to waterproofing project of exposed roofing ,planting roof system ,underground waterproofing of proteiform buildings ,washing room ,basement ,tunnels ,grain depot , subway and reservior.

 


Technical Index > > > 

Performance Conforms to Requirements of TPO Waterproof Membrane (GB27789-2011)

No.

Test item

Requirement

H

L

P

1

Thickness of the resin layer on the middle fabric,mm≥

--

0.40

2

Maximum tension , (N/cm)≥

--

200

250

Tensile strength,MPa≥

12.0

--

--

3

Elongation at maximum tensile strength ,%≥

--

--

 

Elongation at break ,%≥

500

250

--

4

Dimensional change after heat treatment ,%≤

2.0

1.0

250

5

Flexibility at low temperature 

-40℃  no cracks

6

watertightness

0.3MPa,2h   impervious

7

Shock resistance 

0.5kg,m,no seepage 

8

Resistance to static loading 

--

20kg no seepage 

9

Joint peeling strength ,(N/mm)

4.0 or sheet bad

3.0

10

Right angle tear strength,N≥

60

--

--

11

Trapezoid tear strength ,N≥

--

300

450

12

Water absorbency(700c,168h),%≤

After soaking≤

4.0

After hanging≥

4.0

13

Heat ageing (115℃)

Time 

672h

Appearance 

No bubble ,crack,delamination,bond and void

Elongation at maximum tensile strength

,%≥

90

Percentage elongation,%≥

90

Flexibility at low temperature

-40℃ no crack

14

Chemical resistance 

Appearance 

No bubble ,crack,delamination,bond and void

Tensile strength (maximum tensile strength)retention rate,%≥

90

Percentage elongation ,%≥

90

Flexibility at low temperature 

-40℃no crack

15

Artificial weather accelerated aging

Time 

1500hb

Appearance 

No bubble ,crack,delamination,bond and void

Elongation at maximum tensile strength

,%≥

90

Percentage elongation,%≥

90

Flexibility at low temperature

-40℃ no crack 

A、 Resistance to static loading is only applied to requirement of material for pressed roofing  .

b 、The artificial weather time if product for single-layer sheet roofing is 2500h.

 

 

 

Construction Technique of TPO Waterproofing Membrane > > > 

Construction essentials of mechanical fastening system
     Treatment of base course
The base course shall be smooth, dry, clean, crack, without hollow bump. It must be free from water, ice or snow to avoid absorption of moisture from the new roof or roofng system. Before pavement of the membrane, the debris and foreign matters shall be removed from the base course.
    Pre-pavement of TPO membrane: the membrane shall be paved at the designated position and it should be smooth and straight. However, it cannot be tensiled with great force.
    Mechanical fastening of the membrane beneath the overlapping part
Fasten the membrane with fastening components, the space between fastening components shall depend on the local wind speed, type of structural base, height of building and width of the membrane, falling shorter than 600mm. TPO membrane shall be fully bonded within 800 mm around it. 

Furthermore, the membrane shall be fastened at the part of roofing with variations of
height, and at the extrusions on side wall, the skylight, deformation joint, the surrounding
area around the internal corner on the base course where slope exceed 1/6, around the
pipes and at the groove where sealant is poured.
    Welding by hot air
    The TPO membrane should be welded with hot air by automatic hot-air welding
machine or manual hot-air welding machine and silicone rubber roller. At the intersection
of joints, use silicone rubber roller to roll the joint. The irregularity of the surface caused by
TPO membrane with multiple layers may cause cold or false weld.
Construction essentials of the full bonding system
1. The glue shall be painted evenly on the base course and both surfaces of TPO, without the base course exposed to the air, without heap. (Strip adhesion, spot adhesion or border adhesion are acceptable.)
2. The overlapping part shall be welded. First, start with long joints, and then the short
joint
3. Adhesive bonding are applicable to buildings with cement concrete base. The
construction technique and key process are similar employed in handling high polymer
waterproofing membranes of various kinds.

 

 

 